When Mr. Dong's hinge workpiece is produced with barrel nickel brightener, although there is a slight blackening phenomenon in the low current area of the coating, the customer can barely accept it.Recently, a customer has a batch of battery shell workpieces that yellow and rust in the low current area after barrel nickel plating, which makes the customer very dissatisfied.So Mr. Dong wanted to find a barrel nickel plating brightener with good deep plating ability.
Mr. Shi was introduced by a friend to use the medium phosphorus electroless nickel plating additive, but after using this additive, the plating solution is prone to floccules, resulting in a large amount of potion and a short service life of the plating solution.So Mr. Shi wanted to find a medium phosphorus electroless nickel plating additive with better performance.
Mr. Pan from Xiamen, Fujian is the owner of an electroless nickel electroplating factory.Recently, in the process of using medium phosphorus electroless nickel plating solution, Mr. Pan found that the deep plating ability of the deep hole workpiece coating is relatively poor, which affects the performance requirements of the workpiece.So Mr. Pan asked Bigolly engineers whether this electroless nickel plating solution was not easy to use.
Some time ago, in the production process of bright tin plating of a batch of precision hardware, the coating always appeared foggy and not bright.The brightener supplier did not solve the problem after processing the plating solution, which seriously affected the appearance and performance of the workpiece, and the customer did not accept it.This gave Mr. Zhang a headache, so he wanted to replace a better-performing sulfate tin plating brightener.
Recently, Mr. Lin always has the phenomenon of blistering in the coating of the workpiece after using the alkaline zinc-nickel alloy additive.So Mr. Lin wanted to find an alkaline zinc-nickel alloy additive that is not easy to foam.
Mr. Fu is the owner of an electroless nickel plating factory in Xingtai, Hebei Province.Some time ago, Mr. Fu's customer sent a batch of pasta machine parts to be plated with medium phosphorus chemical nickel, but these parts were complained and returned because of the poor wear resistance of the coating and always failed to meet the performance requirements the customer wanted.Mr. Fu didn't want to lose this big customer, so he wanted to find an electroless nickel plating solution with good wear resistance.