Mr. Peng from Guangzhou is the boss of a nickel plating factory.Recently, in the process of nickel plating, Mr. Peng found that the nickel plating layer of several customers' carborundum molds had poor brightness and no wear-resisting phenomenon, which seriously affected the appearance quality and function of these molds.So Mr. Peng is eager to find a nickel plating additive with excellent performance.
Sometimes, the bath is very unstable during the tin plating process, which will seriously affect the performance and quality of the workpiece coating.At this time, we should try a new tin plating additive.
Recently, Mr. Xie found the acid zinc plating additive used in the production process, and the stability of the plating solution is relatively poor. When the workpiece is passivated with color zinc, the adhesion of the coating is poor and the film is easy to fall off.This leads to poor production efficiency and high production costs.Therefore, Mr. Xie is eager to change a better acid zinc plating additive.
Recently, When using nickel plating additive, Mr. Qin found that the thickness of nickel plating layer of the plated workpiece was 5μm. When riveting, the nickel layer will crack, which seriously affects the performance of the workpiece.However, Mr. Qin checked the production processes, concentration of plating solution components and operating parameters, which were normal.What is the problem?
Recently, Mr. Weng found that the brightness of the workpiece coating was poor during the process of using the tin plating additive, and there was color fading during placement, which would increase the resistance of the coating and affect the performance of the workpiece.So Mr. Weng wants to find a tin plating additive with good brightness and no fading.
Mr. Fang received a connector for aircraft, and the workpiece coating needs 20 μm thickness.However, after electroless nickel plating on the workpiece, the coating is brittle and magnetic, which does not meet the customer's requirements.The additive supplier still has such problems after treating the bath for many times, so Mr. Fang wants to find a high phosphorus electroless nickel plating additive that meets the customer's requirements.