Guangdong Bigely Technology Co.,Ltd.
English English
  • Español
  • Português
  • Portugiesisch
  • Français
  • 日本語
  • Български
  • 한국어
  • Türkçe
  • Nederlands
  • English
  • Eesti
  • Suomi
  • বাঙ্গালি
  • беларуская
  • Ελληνικά
  • Kreyòl ayisyen
  • עִברִית
  • हिन्दी
  • Magyar
  • íslenskur
  • Gaeilge
  • italiano
  • Hrvatski
  • Latinus
  • latviski
  • Melayu
  • Malti
  • Монгол
  • မြန်မာ
  • فارسی
  • Polski
  • عربي
  • Română
  • русский
  • slovenský
  • Slovenščina
  • Afrikaans
  • svenska
  • dansk
  • український
  • o'zbek
  • Cymraeg
  • Zulu
  • Tiếng Việt
  • bosanski
  • Deutsch
  • eesti keel
  • ไทย
+86-0663-8291627
CasonChen@bigelaizincplating.com
Sitemap
Guangdong Bigely Technology Co.,Ltd.
  • Home
  • About Us
  • Products
    • Post-treatment products
    • Zinc-Nickel Alloy Plating Series
    • Plastic electroplating additives series
    • Chemical plating product series
    • Galvanized Additives series
    • Tin Plating Additive Series
    • Chrome Plating Additive Series
    • Nickel Plating Additive Series
    • Copper Plating Additive Series
    • Pre-treatment product series
  • News
    • Common problem
    • Electroplating encyclopedia
    • Entreprise news
    • Industry news
  • Download
  • Send Inquiry
  • Contact Us
News
Home > News

News

  • Common problem

  • Electroplating encyclopedia

  • Entreprise news

  • Industry news

New Products

  • Degreasing and dewaxing powder
    Degreasing and dewaxing powder
  • In addition to wax powder
    In addition to wax powder
  • Zinc alloy electrolytic degreasing powder
    Zinc alloy electrolytic degreasing powder
  • Rack nickel brightener
    Rack nickel brightener
  • Bright tin plating additives
    Bright tin plating additives
  • Electroless Nickel Process
    Electroless Nickel Process
Products

News

  • A method to reduce the content of trivalent chromium in plating solution when chromium plating additive is used

    A method to reduce the content of trivalent chromium in plating solution when chromium plating additive is used

    In the process of using chromium plating additives, sometimes the content of trivalent chromium in the plating solution will increase, resulting in the workpiece coating rough, dark, poor brightness and other problems.So how do we reduce the content of trivalent chromium in the bath?

    Wed Nov 16 10:37:52 CST 2022

    Read More
  • Reasons for the color of workpiece appearance in the production process of using zinc nickel alloy black passivator

    Reasons for the color of workpiece appearance in the production process of using zinc nickel alloy black passivator

    A customer inquired that during the use of zinc nickel alloy black passivator, the passivation of the workpiece was followed by sealing treatment, and the appearance of the passivation film would be colored.The workpiece is uniformly black and bright before, how can it be colored?

    Wed Nov 09 08:51:02 CST 2022

    Read More
  • When nickel sulfamate additive is used for production,these 5 points shall be noted for long burrs on the workpiece edge coating

    When nickel sulfamate additive is used for production,these 5 points shall be noted for long burrs on the workpiece edge coating

    In the production process of using nickel sulfamate additive, nickel sulfamate coating is favored by customers because of its good appearance, low stress, fast deposition rate and low porosity.In the production process, some workpieces have burrs on the edge of the coating. What causes this?

    Fri Nov 04 09:06:07 CST 2022

    Read More
  • In the process of using nickel plating additives, pay attention to the following five points:

    In the process of using nickel plating additives, pay attention to the following five points:

    In the process of using nickel plating additives, sometimes the adhesion of the double-layer nickel layer of the workpiece is poor, and the performance test is unqualified. What is the cause?

    Mon Oct 31 10:09:00 CST 2022

    Read More
  • The Effect of Iron Ion on the Bath in the Production of Methanesulfonic Acid Tin Plating Additive

    The Effect of Iron Ion on the Bath in the Production of Methanesulfonic Acid Tin Plating Additive

    In the process of using the additive for methanesulfonic acid tin plating, the concentration of iron ions in the plating solution is constantly accumulating with the progress of production. What is the impact of iron ions on the methanesulfonic acid tin plating solution?

    Wed Oct 26 09:51:00 CST 2022

    Read More
  • When using nickel plating brightener for production, in order to prevent pinholes in the coating, these four points should be noted during electroplating

    When using nickel plating brightener for production, in order to prevent pinholes in the coating, these four points should be noted during electroplating

    When we use nickel plating brightener for production, sometimes the workpiece is very clean in the pretreatment, but the coating has pinholes after nickel plating.So what causes the pinhole phenomenon of the coating?

    Tue Oct 18 08:30:10 CST 2022

    Read More
Links
  • > Google Plus
  • Facebook
  • Twitter
  • LinkedIn
  • Skype
  • WhatsApp
  • YouTube

About Us

  • Home
  • About Us
  • Products
  • News
  • Download
  • Send Inquiry
  • Contact Us

News

  • Common problem
  • Electroplating encyclopedia
  • Entreprise news
  • Industry news

Contact Us

  • No. 5, Tiandongqiao Road, Xilin Industrial Zone, Rongcheng District, Jieyang City, Guangdong Province, China
  • +86-0663-8291627
  • CasonChen@bigelaizincplating.com

QR Code

©Copyright 2022-2025 Guangdong Bigely Technology Co.,Ltd.