In the plating process of aluminum and zinc alloy workpieces, the chemical degreasing treatment before plating is a crucial part. In order to ensure the quality of the plated layer and reduce the failure rate of the plated layer, we must strengthen this treatment. This article will briefly explain the importance of chemical degreasing.
Some customers asked that in the production process of using zinc-nickel alloy colored passivator, the passivation film of the workpiece appeared black phenomenon, what is the cause of this?
With the continuous development of science and technology, the electroplating industry is also improving and innovating. Bigely electroplating zinc-nickel alloy blue passivator is an important raw material in the electroplating process, which has become a new favorite in the electroplating industry with its good performance and ideal anti-corrosion effect. So, how exactly does Bigely electroplating zinc-nickel alloy blue passivator help to improve the corrosion resistance of electroplated products? This article will analyze the following aspects.
After we perform palladium activation in the plastic plating process, we also need to perform accelerating. What is the main function of the accelerating? What kind of electroplating accelerator do we need to choose? Let's discuss these two questions in this article.
In the plastic plating process, the quality of the plating layer is very important, among which pinholes and pitting are common defects, which directly affect the appearance and service life of plastic products. To solve these problems, Bigely developed the roughening additive PL-2, which has shown good results in the application of plastic plating.
Electroless copper plating is a process in which copper ions are reduced by reducing agent and deposited on the surface of conductive substrate without current. The brightness of the coating is one of the important indexes to measure its quality. In order to achieve high brightness of the coating, the choice of additives is very important. The MID rapid electroless copper plating additive HS-ECu-801 developed by Bigely has become the ideal choice for many electroplating plants to pursue high brightness coatings due to its good performance.