Nickel sealing additives

Especially suitable for multi-layer nickel plating process with strict anti-corrosion performance.<br> Contain an amount of conductive particulate additive is not uniformly distributed on the bright nickel layer, ( . 3 million or more pores / cm), so that the chromium layer is formed on the porous chromium, thereby improving the corrosion resistance.

Send Inquiry


Product Description

Nickel sealing additives

Ni-351 nickel sealing additive

(1) Features :

1.Especially suitable for multi-layer nickel plating process with strict anti-corrosion performance.

2.Contain an amount of conductive particulate additive is not uniformly distributed on the bright nickel layer, ( . 3 million or more pores / cm), so that the chromium layer is formed on the porous chromium, thereby improving the corrosion resistance.

3.The plating solution has high stability, long treatment cycle, simple operation, and can greatly reduce the thickness of the coating under the same corrosion performance requirements.

(2) Solution composition and operating specifications

Nickel Sulfate

300 g / l

Nickel chloride

40 g / l (or sodium chloride 17 g / l)

Boric acid

40 g / l

Brightener Ni-351 A

5-6 ml / liter

Softener Ni-351 B (cylinder opening agent)

5-6 ml / liter

Dispersant Ni-351 C (opening agent)

6-8 ml / liter

Solid particles Ni-351 D

10-15 g / l


55 ℃± 5 ℃



Cathode current density

5 ± 1 ampere / square decimeter


1-3 minutes


Nickel plate without anode bag


Air agitation


No continuous filtration required

(3) Solution preparation         

1. Pour two-thirds of the water into the spare tank (or preliminary tank) and heat it to 66 ℃.   

2. Add the required nickel sulfate and nickel chloride, stir to completely dissolve.   

3. Or nickel carbonate was added 4% sodium hydroxide solution to adjust the pH ( the PH value) to 5.2 . 

4. Add 2.5 ml / l of hydrogen peroxide, diluted with water prior to addition to the small number of stirring time.   

5. Add 2.5 g/L of activated carbon , stir for several hours, and then let it stand overnight.   

6. Use a filter pump to filter the plating solution into a clean plating tank.   

7. Add the required boric acid, dissolve it with hot water, and keep the tank stirring for complete dissolution.   

8. Add dilute sulfuric acid and adjust the pH value to 3.8-4.5.   

9. Use a corrugated cathode and a low current density ( 0.15-0.4 ampere/dm2) for continuous electrolysis for more than 12 hours, until the low-level color of the corrugated board coating changes from dark black to light gray or white uniform.

10. After adding the above Ni-351 additives, you can start trial plating.


(4) The function of raw materials

  Nickel Sulfate

  Nickel sulfate is the main source of nickel ions, and the metallic nickel deposited on the plated parts is reduced by nickel ions.

  Nickel chloride

  Nickel chloride provides chloride ions to help the anode dissolve, reduce anode polarization, increase the conductivity of the plating solution, and make the cathode have a higher current density, while also supplying nickel ions.

  Boron acid

  The concentration of boric acid is important for maintaining pH, uniform coating, adhesion and softness. It should not be lower than 40 grams. Boric acid is added after the end of the work day on the basis of analysis due to its consumption.

             (5) Solution maintenance

     Microporous nickel, due to the introduction of hydroxide radicals and various impurities absorbed by solid particles, and the gradual accumulation of anode slime, will deteriorate the performance of the plating solution. Like the bright nickel plating solution, after a period of production, a major treatment is required. However, bright nickel porous nickel has its special place, microporous chrome plating of a very short ( 1-3 minutes), and therefore, if some mechanical impurities bath (diameter larger) will not be deposited on the workpiece , The formation of rough particles. On the other hand, anode bags cannot be used for microporous nickel anodes, so that solid particles can be better dispersed in the plating solution, but the chance of nickel anode mud entering the bath increases. Particles and mechanical impurities sink to the bottom of the tank, the clear liquid is drawn out, and hydrogen peroxide and activated carbon are added to the clear liquid for treatment. (Same method as bright nickel treatment) Then add various additives according to the formula amount, adjust the pH value, and then continue production. Discard the solid particles, mechanical particles and anode mud at the bottom of the tank.

Microporous nickel plating solution has the same allowable amount of impurities as bright nickel. The pollution of heavy metal impurities can also be removed by low current electrolysis.

It must be emphasized that the introduction of organic impurities will greatly reduce the density of micropores. Therefore, the raw materials for preparing a new bath must pay attention to the content of organic impurities. Unsaturated hydrocarbons, pyridines, and epoxy condensates are brought into the bright nickel plating solution as brighteners and have little effect on microporous nickel. The introduction of the wetting agent in the bright nickel does not affect the micropore density and appearance. Therefore, it can be considered to directly transition from bright nickel to microporous nickel without washing in the middle.

For units that are not in continuous production, the production will stop for a long time, and all solid particles will sink to the bottom of the tank. When production is resumed, air stirring must be carried out for about 1-2 hours, and the particles can be fully stirred before production can begin.

Proved by many manufacturers and use, the tank liquid is very stable, and it is only treated once every half a year, and there are few failures .

After testing and accumulating experience in the production practice of multiple factories , the consumption of various additives is as follows:


Ni-351 A

Right amount

Ni-351 B

Right amount

Ni-351 C (additive)

400-500 ml / kA per hour

Ni-351 D

200-300 ml / kA per hour

     As long as the above consumption is supplemented, the appearance of the coating and sufficient particle density can be guaranteed.


(6) Safety warning:

Bigley recommends that you read the material safety information of this product before using this product. The material safety data sheet can be obtained from the company.


(7) Purchasing information

product name

product code


Microporous Nickel Tim additives

Ni-351 A

20 kg

Ni-351 B

20 kg

Ni -351 C

20 kg




1. Q: Do you make the products yourself? Are you a trader or a manufacturer?

     A: Yes, the products are produced by our company. Our company is a manufacturer focusing on the R&D and manufacturing of environmental protection electroplating additives. Our factory has 5000 square meters with an annual capacity of 15000 tons.

2. Q: Can your company send samples for trial?

     A: We can provide samples for trial.

3. Q: What is the quality of your products?

     A: Our company all products core raw materials is used by Germany BASF, American Dow Chemical and other international brand products. The production process is strictly in accordance with the ISO9001 quality management system, from the incoming inspection, product inspection, according to the strict inspection standard, ensure that every drop of products qualified. Product quality you can rest assured, like BYD, Huawei, Foxconn such enterprises are also using our products.

4. Q: How long is the shelf life of your products?

     A: The shelf life of our products is two years. If you do not use up the products within a short time after you buy them, we suggest you store them in a cool place, not in the sun or in a high temperature environment.

5. Q: Are your products environmentally safe?

     A: Our products have passed the SGS test and are recognized as "Green and Environment-friendly Promotion Products". Many auto parts and electronic products which use our products can pass the strict environmental protection test when they are exported to Europe and America. Therefore, we can be trusted in terms of environmental protection and safety.

6. Q: Can your company provide technical services?

     A: Yes, our company has a technical service team of more than 10 people. The technical engineers all have more than 20 years' experience in electroplating factory. They can provide customers with comprehensive technical of pre-sales and after sales.

7. Q: Is it possible to visit your company?

     A: Yes, of course. You are very welcome! We can meet you at Jieyang airport, If you can come to our city. Also you can visit our factory through live video.

8. Q: Can you customize products according to our needs?

     A: Yes, our company has research and development strength, the product formula derived from Europe and the United States laboratory, European and American engineers technical support, work together with domestic universities. Our company has a member of Guangdong province expert enterprise workstation, Shantou university science and technology correspondent workstation, Jieyang city environmental protection e

Product Tag

Related Products

Send Inquiry

Should you have any enquiries, please kindly fill in the Enquiry Form below . We will reply you within 24 hours.