Mr. Li from Huizhou, Guangdong is the owner of an electroplating factory engaged in chemical nickel plating processing of various precision automotive parts, mobile phone metal shells, and other workpieces. Recently, Mr. Li's workpieces have always been complained by customers about the poor welding performance of the chemical nickel coating. Due to the large number of returned workpieces, Mr. Li's solution supplier has not been able to solve this problem after multiple treatments of the plating solution. So Mr. Li wanted to search online for a chemical nickel plating solution with better welding performance.
On this day, Mr. Li saw Bigley's chemical nickel plating solution Ni-809 while searching online. He inquired about the characteristics and operating parameters of this solution, as well as the welding performance of the chemical nickel coating on the workpiece. After understanding Mr. Li's production situation, engineers from Bigley explained to him that some chemical nickel potions on the market have poor chemical stability due to outdated technical formulas. During the production process, the plating solution will age faster, and the content of sodium phosphite in the plating solution will gradually increase. As a result, the phosphorus content of the coating will increase, leading to a decrease in the welding performance of the coating. In addition, some chemical nickel solutions may incorporate metal additives, which have a significant impact on the welding performance of the coating.
Bigley's chemical nickel plating solution Ni-809 is a product that has been improved through technical formula, without adding metal additives, and is produced using imported raw materials. It has good chemical stability, and the plating solution remains clear after long-term production. The service life of the plating solution is as long as 12-14 cycles. The chemical nickel coating on the workpiece is uniform and bright, with excellent hardness, wear resistance, and corrosion resistance, especially with good welding performance, which can meet various high-quality requirements for chemical nickel plating on the workpiece. Mr. Li is quite interested in this potion, so he decided to buy one bucket first to try it out.
Under the guidance of the engineer, Mr. Li used this chemical nickel solution Ni-809. The coating on the workpiece was uniform and bright, and the phosphorus content remained stable at 7.5-9%. The workpiece also passed the welding performance test. The plating solution is also more stable than before, less prone to turbidity, and the lifespan of the plating solution can be doubled compared to the previous one, saving production costs even more. Soon, Mr. Li placed another order and signed a cooperation agreement with Bigley.
So, our workpiece has poor welding performance during the process of chemical nickel plating. It's worth trying Bigley's chemical nickel plating solution Ni-809 to effectively improve the quality of the coating and save production costs. If you are interested in this chemical nickel plating solution, please contact Bigley customer service for free samples and detailed technical information!