Neodymium iron boron workpieces are prone to rust and poor adhesion when plated with nickel. Try this electroless nickel plating agent quickly.

Neodymium iron boron workpieces are prone to rust and poor adhesion when plated with nickel. Try this electroless nickel plating agent quickly.

Tue Mar 28 16:37:17 CST 2023

Mr. Tang's company is a factory in Shenzhen that produces NdFeB workpieces and processes them himself. He also has his own nickel barrel plating production line. However, during the nickel plating process, Mr. Tang's neodymium iron boron workpiece found that the workpiece needs to be charged into the groove immediately after activation, and a large current impact should be used to make the part plated as soon as possible. Despite this, the workpiece is still prone to oxidation during the production process, and the adhesion of the plating layer is relatively poor. It happened that one day, Mr. Tang saw Bigley's electroless nickel plating agent and wanted to change the production process.

On that day, Mr. Tang saw the operation video of Bigley's electroless nickel plating agent Ni-809 while searching online. After simple pre-treatment, the workpiece was placed in the plating solution to be plated. Mr. Tang wondered if his workpiece could also be operated in this way, so he consulted Bigley engineers in detail about the production process and coating performance of this chemical nickel potion. Mr. Tang is very interested in this production process, so he wants to try it on his own.

Mr. Tang opened a 300-liter electroless nickel plating tank on the production line and conducted production under the guidance of an engineer. After Mr. Tang used this chemical nickel production process, the production operation became simple and feasible, greatly reducing the technical threshold for operators. As long as the temperature, pH value, and concentration of the concentrated solution were well controlled, the requirements for continuous production from single shift to multiple shifts could be met, with stable output and high production efficiency. Currently, coatings with a thickness of 10-12 microns have good adhesion, can meet the 96 hour salt spray requirements, and are not easily oxidized and discolored. In addition, after Mr. Tang used the chemical nickel production process, the production cost was greatly reduced due to avoiding the waste of raw materials required for the device during nickel plating.

Therefore, when plating nickel on NdFeB workpieces, the plating layer is prone to rust and poor adhesion. Try Bigley's electroless nickel plating agent Ni-809 quickly to effectively improve the performance and quality of the plating layer and greatly reduce production costs. If you are interested in this chemical nickel lotion, please contact Bigley Customer Service for free samples and detailed technical information!