Mr. Zhou is the owner of a home appliance plating factory in Yuncheng, Shanxi. His production line mainly focuses on the processing and production of phosphorus chemical nickel plating technology for electronic accessories. Recently, Mr. Zhou's plating solution has always experienced a phenomenon where after 8 cycles of use, the workpiece will turn black after being plated with chemical nickel. The solution supplier has made several adjustments, but the problem remains unresolved. So Mr. Zhou was wondering if there was a problem with the use of medium phosphorus chemical nickel plating solution.
One day, Mr. Zhou searched online and found Bigley's medium phosphorus electroless nickel plating solution Ni-809, and consulted engineers in detail about the characteristics of this solution. After understanding the problems that Mr. Zhou had encountered, the engineer patiently explained to Mr. Zhou that some chemical nickel plating solutions on the market have technical defects. When the solution is used for 6-8 cycles, some effective components in the plating solution will fail, resulting in insufficient density of the chemical nickel coating and gaps. When in contact with air, the coating is prone to oxidation and nickel rust, which is the phenomenon of blackening.
And Bigley's medium phosphorus chemical nickel plating solution Ni-809 is a joint venture with European and American laboratories, with technical support from European and American engineers. The raw materials are products from German brands such as BASF, ensuring high purity, low impurities, and good stability of the plating solution. After 12 cycles of use, the workpiece coating will not appear black. So Mr. Zhou first purchased a small amount of liquid medicine for testing.
Under the guidance of the engineer, Mr. Zhou used this solution for testing. The plating solution was used for 12 cycles, 14 cycles, and until the plating solution was scrapped, there was no blackening of the workpiece. Mr. Zhou repeated the tests three times and found no blackening of the coating on the workpiece. Therefore, Mr. Zhou signed a procurement contract with Bigley.
So, when our workpiece is prone to blackening after multiple cycles of using the plating solution during the process of electroless nickel plating, it is advisable to try this medium phosphorus electroless nickel plating agent Ni-809. If you also want to find such a medium phosphorus chemical nickel plating solution, you can contact Bigley customer service to obtain free samples and detailed technical information!
If you want to learn more about chemical nickel, you can click to view the "Common problem".