After using acid copper plating brightener, the workpiece can obtain a coating with mirror brightness, strong ductility and flatness.Sometimes, the color of the coating will quickly become dark or brown after the workpiece is coated with acid copper. What is the reason?
A customer asked that when using nickel plating additives for production, some electronic products are coated with nickel, and then the tin coating is easy to fall off during tin plating. What is the reason?
In the process of using zinc nickel alloy color passivator, sometimes the passivation film of the workpiece after passivation is not firm, and it is easy to be wiped off.What causes this?
In the process of using zinc nickel alloy brightener, we need to control the concentration of zinc ion, nickel ion and sodium hydroxide in the bath to obtain protective zinc nickel alloy coating with high decorative and corrosion resistance.Sometimes the nickel content in the coating of the workpiece is too high. What causes this?
When we use medium phosphorus electroless nickel plating solution for production, there is such a phenomenon: the nickel layer will produce by-products of phosphite during the deposition process. With the production, the concentration of phosphite will become higher and higher, so the reaction rate of electroless nickel plating will be affected and gradually reduced.The deposition rate of the plating solution at the initial and final stages will have a large deviation, so how can we reduce this deviation?
When we use nickel sulfamate additive in the production process, sometimes the brittleness of the nickel coating is large, which affects the performance and quality of the coating.What causes the brittleness of nickel sulfamate coating?