Some customers ask that in the production process of tin plating brightener, the stability of the plating solution can be good, so that the workpiece can get good ductility, solderability and corrosion resistance. So how do we operate in order to make the plating of the stability of good performance, and can effectively extend the service life of the plating solution?
The use of high sulfur nickel additives can obtain nickel plating with sulfur content of 0.12%~0.25%, which is mainly used for the protection of steel, zinc alloy substrate and the intermediate layer of decorative plating, and can effectively improve the corrosion resistance of the plating. So how should we maintain the plating solution when using high sulfur nickel additives?
Irregular blistering on the whole workpiece, normal color of the base metal on the reverse side of the plated layer, must it be related to the alkaline copper plating additives? Not necessarily, it may be caused by the imbalance of the ratio of tank solution components.
In the production process of using chrome plating additives, we often encounter a headache, that is, the leakage of plating solution, which causes a lot of trouble to the waste water and exhaust gas treatment. So how can we avoid the leakage of plating solution in the production?
In the process of using nickel plating brightener, due to the crystallization of nickel metal has a certain deformation or heterogeneous impurity, it will produce a certain amount of internal stress in the plating layer. When the internal stress of the nickel layer is large, the hardness of the plating layer will be larger, but easy to peel, crack or poor ductility. So, what are the factors related to the internal stress of the nickel layer?